Descrition:
Copper Plate/Sheet/Coil including the following Style:
Hot Rolled sheet
Standard: GB/ASTM/JIS/DIN Grade: T2, T3, TP1, TP2/C11000, C12500, C12000, C12200/C1100, C1201, C1220/E-CU58, 1/2 W-Cu, SF-Cu
Temper: R
Thickness: 4mm~150mm
Width: 200mm~3000mm
Cold Rolled sheet
Standard: GB/ASTM/JIS/DIN
Grade: T2, T3, TP1, TP2/C11000, C12500, C12000, C12200/C1100, C1201, C1220/E-CU58, W-Cu, SF-Cu
Temper: Y, Y2, M
Thickness: 0.2mm~10mm
Width: 200mm~3000mm
Special Pure Copper sheet
Standard: GB/ASTM/JIS/DIN
Grade: T2, TP2/C11000, C12200/C1100, C1220/E-CU58, SF-CU
Temper: M, Y, Y 2, Y4
Thickness: 0.3mm~10mm
Width: 200mm~3000mm
Oxygen Free Copper sheet
Standard: GB/ASTM/JIS/DIN
Grade: TU1, TU2/C10200, C1020/OF-CU /
Temper and Thickness: R: >=4mm
Y, Y2, M: 0.2mm~10mm
Width: 200mm~3000mm
We are capable of producing a wide variety of precision strip products to special requirements, and is geared to handle high volumes with tight tolerances. Continuous strip-casting machines produce long, weld-free coils of uniform composition and properties, and automatic electronic gauge-controls maintain consistent thickness.
Application
copper sheet Can be made to do all sorts of deep drawing and bending stress components, such as manufacturing pins, rivets, gasket, nuts, conduits, the barometer spring, screen, radiator parts, etc
Specification
|
Copper alloy
|
Material
|
Temper
|
Dimensions (mm)
|
The main properties
|
|
Thickness
|
Width
|
Length
|
|
C11000
C12200
C10500
C10200
|
Hot Rolled
|
Hot rolled
|
4~8
|
600~2000
|
4000 max.
|
High Conductivity.
When thickness: 4~14mm,
Rm (min.):195Mpa, A11.3(min.):30%
|
|
8~60
|
600~3000
|
6000 max.
|
|
60~150
|
600~2500
|
4000 max.
|
Don’t provide properties.
|
|
Cold Rolled
|
Soft,H/4,H/2,
Hard,
Extra Hard.
|
0.3~0.5
|
600 max.
|
2000 max.
|
Soft:Rm(min.):205Mpa A11.3(min.):30%.
H/4: Rm: 215~275Mpa A11.3(min.):25%.
H/2: Rm:245~345Mpa A11.3(min.):8%.
Hard: Rm: 295~380Mpa.
Extra Hard: Rm (min.):350Mpa
|
|
0.5~3.0
|
1000 max.
|
2500 max.
|
|
3.0~12
|
3000 max.
|
6000 max.
|
|
Soft,H/8,
H/2,H
|
4~20
|
50~650
|
6000 max.
|
|
H
|
2~10
|
100~1000
|
300~2000
|
|
C10200
|
Oxygen free plates for Copper Stave in blast furnace.
|
Hot Rolled
|
75~150
|
770~1590
|
1400~3600
|
High Conductivity.
|